高密度聚苯硫醚
PPS-HP7MD是一种高密度聚苯硫醚材料,具有密度高,耐化学腐蚀性以及耐热性等特点
本品主要用于汽车、电子电器、化工设备、机械等行业中,制作高密度要求的产品
Physical Property | unit | Testing Standard | Test Result | ||||
Density | g/cm3 | ISO 1183 | 3.15 | ||||
Molding shrinkage-Parallel flow direction | % | ISO 294-4 | 0.4 | ||||
Molding shrinkage-Vertical flow direction | % | ISO 294-4 | 0.7 | ||||
Water absorption rate(23℃,24Hrs) | % | ISO 62 | 0.02 |
Mechanical Property | unit | Testing Standard | Test Result | ||||
Tensile Strength | MPa | ISO 527 | 60.0 | ||||
Flexural Strength | MPa | ISO 178 | 100.0 | ||||
Flexural Modulus | GPa | ISO 178 | 7.0 | ||||
Charpy Impact Strength | kJ/m2 | ISO 179 | 20.0 | ||||
Charpy Notched Impact Strength | kJ/m2 | ISO 179 | 4.0 |
Thermal property | unit | Testing Standard | Test Result | ||||
Melting Point | ℃ | ISO 11357 | 283.0 | ||||
Hot Deformation Temperature(1.8MPa) | ℃ | ISO 75 | 180.0 | ||||
Flame Retardancy | UL-94 | V-0 |
Thermal property | unit | Testing Standard | Test Result | ||||
Dielectric Strength | kV/mm | IEC 60243 | - | ||||
Dielectric Constant | IEC 60250 | - | |||||
Dielectric Loss Factor | IEC 60250 | - | |||||
Volume Resistivity | Ω・cm | IEC 60093 | - | ||||
Comparative Tracking Index | V | IEC 60112 | - |
Injection Molding Conditions | unit | Reference Value | |||||
Drying Tmperature | ℃ | 130-150 | |||||
Drying Time | Hrs | 3-4 | |||||
Heating temperature of cylinder | ℃ | 290-320 | |||||
Nozzle Temperature | ℃ | 300-320 | |||||
Mold Temperature | ℃ | 120-150 | |||||
Injection Pressure | Mpa | 80-150 | |||||
Packing Pressure | Mpa | 30-70 |