Committed to the original development and import substitution of PPS polyphenylene sulfide
Ultra High Wear Resistant Polyphenylene Sulfide
PPS-PAC20 is a 20% carbon fiber reinforced polyphenylene sulfide material with good wear resistance, excellent chemical resistance and heat resistance.
This product is mainly used to make gear, high temperature sleeve, sliding bearing and other products with lower friction coefficient and lower friction consumption requirements.
| Physical Property | unit | Testing Standard | Test Result |
| Density | g/cm3 | ISO 1183 | 1.42 |
| Molding shrinkage-Parallel flow direction | % | ISO 294-4 | 0.3 |
| Molding shrinkage-Vertical flow direction | % | ISO 294-4 | 0.7 |
| Water absorption rate（23℃,24Hrs） | % | ISO 62 | 0.04 |
| Mechanical Property | unit | Testing Standard | Test Result |
| Tensile Strength | MPa | ISO 527 | 100.0 |
| Flexural Strength | MPa | ISO 178 | 200.0 |
| Flexural Modulus | GPa | ISO 178 | 11.0 |
| Charpy Impact Strength | kJ/m2 | ISO 179 | 22.0 |
| Charpy Notched Impact Strength | kJ/m2 | ISO 179 | 5.0 |
| Thermal property | unit | Testing Standard | Test Result |
| Melting Point | ℃ | ISO 11357 | 280.0 |
| Hot Deformation Temperature(1.8MPa) | ℃ | ISO 75 | 260.0 |
| Flame Retardancy | UL-94 | V-0 |
| Wear resistance | unit | Testing Standard | Test Result |
| Sliding friction coefficient | GB/T 3690 | 0.2 | |
| Wear quality | mg/120min | GB/T 3690 | 5.0 |
| Injection Molding Conditions | unit | Reference Value |
| Drying Tmperature | ℃ | 130-150 |
| Drying Time | Hrs | 3-4 |
| Heating temperature of cylinder | ℃ | 290-320 |
| Nozzle Temperature | ℃ | 300-320 |
| Mold Temperature | ℃ | 120-150 |
| Injection Pressure | Mpa | 80-150 |
| Packing Pressure | Mpa | 30-70 |